Mechanical measurements of pure and kaolin reinforced hydroxyapatite-derived scaffolds: A comparative study

D. O. Obada, E. T. Dauda, J. K. Abifarin, N. D. Bansod, D. Dodoo-Arhin

Research output: Contribution to journalConference articlepeer-review

20 Citations (Scopus)

Abstract

This study describes the mechanical properties of pure hydroxyapatite (HAp) and kaolin reinforced hydroxyapatite (K-HAp) produced from non-separated animal bones using compression pressure under different sintering regimes. The HAp microparticles were synthesized separately using a facile heat treatment method and reinforced with 15wt% of beneficiated kaolin (HAp/15wt% BK) using the sol-gel method. The HAp and K-HAp derived scaffolds were fabricated by cold pressing with a compaction pressure of 500Pa. Next, the scaffolds were sintered at 900°C, 1000°C and 1100°C with a 2h dwell time in air atmosphere. Subsequently, the mechanical properties of the scaffolds were examined. The effect of sintering temperature and compaction pressure on the hardness and the compressive strength of the pure and reinforced HAp showed that at all points of measurement (with and without compaction pressure), the mechanical properties increased with an increase in sintering temperature, and the most significant mechanical properties were obtained at 1100°C. The values of hardness at the maximum sintering temperature (1100°C) are 0.93 and 1.09GPa with and without the application of compaction pressure, respectively, for pure HAp-derived scaffolds and 0.74 and 0.78GPa with and without the application of compaction pressure, respectively, for K-HAp-derived scaffolds. The compressive strength for K-HAp had the value of 7.84MPa as compared with 0.69MPa for the non-reinforced HAp matrix with the application of compaction pressure (500Pa). The findings show that the mechanical properties of the synthesized kaolin reinforced HAp in relation to the scaffolds produced with the low compaction pressure of 500Pa is suitable for human trabecular bone.

Original languageEnglish
Pages (from-to)2295-2300
Number of pages6
JournalMaterials Today: Proceedings
Volume38
DOIs
Publication statusPublished - 2020
Externally publishedYes
Event1st International Conference and Exposition on Mechanical, Material and Manufacturing Technology, ICE3MT 2020 - Hyderabad, India
Duration: 9 Oct 202010 Oct 2020

Keywords

  • Compaction
  • Gradient
  • Hydroxyapatite
  • Kaolin
  • Mechanical properties
  • Sol-gel

Fingerprint

Dive into the research topics of 'Mechanical measurements of pure and kaolin reinforced hydroxyapatite-derived scaffolds: A comparative study'. Together they form a unique fingerprint.

Cite this